321 vlekvrye staal strook
Vlekvrye staalplaatplaat Graad Baogu-voorraad
| Tik | Graad | Graad | Chemiese komponent % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Ander | |||
| Austenities | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3,50-5,50 | 5,50–7,50 | ≤0,060 | ≤0,030 | - | ≤1.00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1.00 | - | ≤0,25 | - | ||
| 301 | 1,431 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | ≤0,10 | - | |
| 304 | 1,4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304L | 1,4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 304H | 1,4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24:00-26:00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24:00-26:00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1,4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1,4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1,4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317L | 1,4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1,4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0,70 | |
| 321H | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1,455 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C%-1,10 | |
| 347H | 1,494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0,045 | ≤0,030 | - | ≤1.00 | - | - | Nb≥10*C%-1,10 | |
| xm-19 | Nitronic50 | ≤0,06 | 20.50-23.50 | 11.50-13.50 | 4,0-6,0 | ≤0,045 | ≤0,030 | 1.50-3.00 | ≤1.00 | - | 0,2-0,4 | Nb: 0,10-0,30 V: 0,10-0,30 | |
| 904L | N08904 | ≤0,02 | 19,0-23,0 | 23,0-28,0 | 4,0-5,0 | ≤0,045 | ≤0,035 | ≤1.00 | 0.1 | Cu:1,0-2,0 | |||
| Dupleks | 2205 | S32205 | ≤0,03 | 22,0-23,0 | 4,5-6,5 | ≤2.00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1.00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| * | S32760 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1.00 | ≤0,030 | ≤0,010 | 3,0-4,0 | ≤1.00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0,03 | 21,5-24,5 | 3,0-5,5 | ≤2,50 | ≤0,040 | ≤0,030 | 0,05-0,6 | ≤1.00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1,446 | ≤0,08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0,040 | ≤0,030 | 1.00-2.00 | ≤0,75 | - | - | ||
| Ferriet | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0,5 | ≤1.00 | ≤0,040 | ≤0,020 | - | ≤1.00 | - | ≤0,030 | Ti6(C+N)~0.50 Nb:0.17 |
| 430 | 1Kr17 | ≤0,12 | 16.00-18.00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1.00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1.00 | - | 0,035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| 446 | S44600 | ≤0,20 | 23.00-27.00 | 0,75 | ≤1,5 | ≤0,040 | ≤0,030 | 1,50-2,50 | ≤1.00 | - | ≤0,25 | - | |
| Martensiet | 410 | 1Kr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12.00-14.00 | 3) | ≤1,25 | ≤0,060 | ≥0,15 | - | ≤1.00 | - | - | - | |
| 420 | 2Kr13 | ≥0,15 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Kr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤1.00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15.00-17.00 | 1,50-2,50 | ≤1.00 | ≤0,040 | ≤0,030 | - | ≤0,80 | - | - | - | |
| 440C | 11Kr17 | 0,95-1,20 | 16.00-18.00 | - | ≤1.00 | ≤0,040 | ≤0,030 | 0,75 | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 | 6,50-7,50 | ≤1.00 | ≤0,035 | ≤0,030 | - | ≤1.00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3,50-5,50 | ≤1.00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1.00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Beskrywing
321-vlekvrye staalstrook is 'n tipe austenitiese vlekvrye staal met 'n lae koolstofinhoud en goeie korrosiebestandheid teen baie korrosiewe omgewings.321 bied uitstekende sweisbaarheid, goeie verwerkbaarheid en uitstekende vervaardigingseienskappe.
321 vlekvrye staal strook word algemeen gebruik in die chemiese industrie, pulp- en papierbedryf, mariene en buitelandse ingenieursbedryf sowel as in die voedsel- en drankbedrywe.
321 vlekvrye staal strook het ook 'n hoë vlak van weerstand teen chloriedspanning korrosie krake en putte.Dit is ook bestand teen soutsuur by verhoogde temperature tot 250°C (480°F).
Kenmerke
Goeie korrosiebestandheid: 321 vlekvrye staalstrook het beter korrosiebestandheid as 304 en 316 tipes vlekvrye staal, wat dit ideaal maak vir gebruik in korrosiewe omgewings.
Uitstekende sweisbaarheid: 321 vlekvrye staalstrook kan met alle metodes gesweis word, insluitend boogsweis (TIG/GTAW), elektronstraalsweising (EBW/EFW), onderwaterboogsweis (SAW) en laserstraalsweising (LBIW).
Hoë sterkte: Die sterktevlakke van 321 vlekvrye staalstrook is tot 50% hoër as dié van 304 soorte vlekvrye staal en tot 80% hoër as dié van 316 tipes vlekvrye staal as gevolg van hul verhoogde koolstofinhoud en austenietkorrelgrootte.